Daelim Po1y® XP3200H
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gtFaAw_DaelimPo1yXP3200H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®XP3200H is a metallocene linear low density polyethylene product,. It is available in Europe or Asia Pacific. Daelim Po1y®XP3200H application areas include bags/linings, movies, agriculture, food contact applications and coating applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 60.8 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 49.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 530 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 570 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 130 | g | ASTM D1709A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1004 | ||
| Lateral flow : 0.0300mm | 132 | kN/m | ASTM D1004 |
| Traffic : 0.0300mm | 127 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 109 | °C | ASTM D1525 |
| Peak Melting Temperature | 117 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 89 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 20 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2307FI | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Axiall PVC 8805 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Formolene® 1103k | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Karina CLEAR PVC COMPONUD -E 794-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polyclear® Refresh PET 1101 | Indorama Ventures Polymers México | PET | Polyclear® |