DOMAMID® 6G30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics SPA |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gt6XYE_DOMAMID-6G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, 30% glass fiber reinforced, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | |||
| Across Flow : 23°C, 72 hr | 0.80 to 1.0 | -- | % | |
| Flow : 23°C, 72 hr | 0.30 to 0.50 | -- | % | |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 180 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8500 | 5000 | MPa | ISO 178 |
| Flexural Stress 3 | 270 | 160 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 15 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 80 | 90 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.00 to 3.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 95.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 90.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Catalyst CT/4 BLK | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| ColorRx® TPE-B95A0RXCL | LTL Color Compounders, Inc. | TPE | ColorRx® |
| EPLAMID 6 GFT 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| Hifax HSBM CB 1158 G | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Hapflex™ 566-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |