Silamid® LSV20
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Silamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gt1Ar4_Silamid-LSV20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, type reinforced with 20% short glass fibres, modificated, high toughness at low humidity contents and at temperatures below 0°C , natural, other color shades according to customer's requests, optimal flow properties. Suitable for injection mouldings where increased impact resistance is required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | 1.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow | 1.6 to 1.8 | 1.6 to 1.8 | % | |
| Flow | 0.80 to 0.90 | 0.80 to 0.90 | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | 1.1 | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5700 | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 115 | 70.0 | MPa | ISO 527-2 |
| Flexural Modulus | 4600 | 2300 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+11 | ohms·cm | IEC 60093 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2585A | Teknor Apex Company | TPE | Telcar® |
| TOTAL Polystyrene Crystal CX5243 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Vydyne® 50BWFS | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ACCUCOMP™ CP0402V | ACLO Compounders Inc. | PP Copolymer | ACCUCOMP™ |
| Ketjenflex® MH | Axcentive SARL | Plasticizer | Ketjenflex® |