Andur 9 APLF/Curene® 442
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gsXw37_Andur-9-APLF-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 9 APLF is a polyester based liquid, toluene diisocyanate terminated prepolymer containing 0.1% or less free TDI monomer. An elastomer with a hardness of 90 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442, other diamines or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 6.89 | MPa | ASTM D412 |
| 300% strain | 11.0 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 53.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 590 | % | ASTM D412 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 5.5 | min | |
| Demold Time (100°C) | 20 - 30 | min | |
| Post Cure Time (100°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 88 to 92Die C Tear, ASTM D1004: 485 pliAverage Split Tear, ASTM D1938: 270 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 9 APLF: 170-190°F Curene 442: 230-240°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-93A-B20 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| TAROPRENE® 2 A60 E1G | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Formolene® E-924 | Formosa Plastics Corporation, U.S.A. | HDPE, HMW | Formolene® |
| LARIPUR® LPR 7060 | COIM S.p.A. | TPU-Polyether | LARIPUR® |
| Lumiplas® LD7701FD | LG Chem Ltd. | PC | Lumiplas® |