TAROLOX 200 G6
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gsIEpC_TAROLOX-200-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROLOX 200 G6 is a Polybutylene Terephthalate + ASA (PBT+ASA) product filled with 30% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.30 to 0.50 | % | |
| Flow | 0.20 to 0.40 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.050 | % | |
| Saturation, 23°C | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 8200 | MPa | ISO 178 |
| Flexural Stress 2 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 180 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Melting Temperature | 220 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 20 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2607 | Covestro - Polycarbonates | PC | Makrolon® |
| Trilliant™ HC HC3320-0020 RS Natural | PolyOne Corporation | PBT | Trilliant™ HC |
| Diakon® CLG902L | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| EASYPOXY® K-230 | Cytec Industries Inc. | Epoxy | EASYPOXY® |
| LNP™ THERMOCOMP™ UF0067W compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |