Ultramid® B3EG3 BK00564
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | grpq2H_Ultramid-B3EG3-BK00564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3EG3 BK00564 is a 15% glass fiber reinforced, pigmented black injection molding PA6 grade for housings with enhanced impact resistance. Applications Typical applications include automotive mirror housings and wheels of moutain bikes. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.7 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6060 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 115 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 4.5 | -- | kJ/m² | |
| 23°C | 5.0 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 217 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | 7.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.025 | 0.24 | ||
| 1 MHz | 0.025 | 0.24 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J709QG | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| NEFTEKHIM PE 5122N | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| KRATON® D1119 P | Kraton Polymers LLC | SIS | KRATON® |
| LUVOCOM® 3-7901 | Lehmann & Voss & Co. | Nylon 6 | LUVOCOM® |
| LEXAN™ HFD4413 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |