ESTOPLAST EP 2030BR02
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | ESTOPLAST EP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | grI0Rq_ESTOPLASTEP2030BR02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polybutylene Terephthalate - Glass Fiber Reinforcement, 30% Automotive: Plug and socket Connectors, Head/Tail Lamp Housings Electrical & Electronic: Connectors, Switch Parts, Electrical Enclosure |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 105 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Strength | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 200 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm | HB | UL 94 | |
| 1.5 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 235 - 240 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 240 - 250 | °C | |
| Mold Temperature | 100 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mylar® A (1000 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Baytec® U1281XA | Covestro - PUR | TSU | Baytec® |
| Evermore PUR SS-1345 | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Hostacom X M2 T28 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| Sylvin 5417-85 Natural | Sylvin Technologies Incorporated | TPE | Sylvin |