Diakon® ST25G8
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | grGqDx_Diakon-ST25G8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diakon®ST25G8 is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion. Diakon®The main features of ST25G8 are:
Diakon®The typical application field of ST25G8 is: automobile industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 2.5 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.32 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 71 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 15 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.9 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 42 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 3.6 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 111 | °C | ISO 306/A |
| -- | 102 | °C | ISO 306/B |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 91.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Mold Shrinkage, H961/30: .4 to .7% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50.0 - 80.0 | °C | |
| Rear Temperature | 190 - 240 | °C | |
| Middle Temperature | 210 - 260 | °C | |
| Front Temperature | 210 - 280 | °C | |
| Nozzle Temperature | 220 - 270 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 34S5150 | The Matrixx Group, Inc. | PBT | Matrixx |
| Ultraform® N 2320 U03 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| APEX® 01-A0383A-85 | Teknor Apex Company | PVC, Flexible | APEX® |
| Expandable PS F11MB-n | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| INSTRUC PPSLGFMIN65 | Infinity LTL Engineered Compounds | PPS | INSTRUC |