Generic Nylon 11
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqyENs_Generic-Nylon-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 11 This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.02 - 1.05 | g/cm³ | ASTM D792 |
| -- | 1060 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate | 1.69 | cm³/10min | ISO 1133 2 |
| Water Absorption | |||
| 23°C, 24 hr | 0.29 - 0.31 | % | ASTM D570 |
| Saturated, 23°C | 1.1 - 1.9 | % | ASTM D570 |
| Saturation | 1.9 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 78 - 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1110 | MPa | ISO 527-2 4 |
| Tensile Stress | |||
| Yield | 35.5 | MPa | ISO 527-2 5 |
| Fracture, 23°C | 40.0 - 69.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 10 - 17 | % | ASTM D638 |
| Yield | 23 | % | ISO 527-2 6 |
| Fracture, 23°C | 280 - 410 | % | ASTM D638 |
| Tensile Elongation at Break | 49 - 50 | % | ISO 527-2 7 |
| Flexural Modulus (23°C) | 288 - 1380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 8 | ||
| -30°C | 8.54 | kJ/m² | ISO 179/1eA |
| 23°C | 9.10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 40 - 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa | 137 | °C | ISO 75-2 9 |
| 1.8 MPa, not annealed | 41.0 - 54.6 | °C | ASTM D648 |
| 1.8 MPa | 47.6 | °C | ISO 75-2 10 |
| Vicat Softening Temperature (50°C/h, B (50N)) | 159 | °C | ISO 306 11 |
| Melting Temperature | |||
| -- | 186 | °C | |
| -- 12 | 187 | °C | ISO 11357-3 13 |
| CLTE - Flow | 9.8E-5 | cm/cm/°C | ISO 11359-2 14 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+11 - 1.0E+14 | ohms | IEC 60093 15 |
| Volume Resistivity | 1.0E+2 - 1.3E+12 | ohms·m | IEC 60093 16 |
| Electric strength | 30 | kV/mm | IEC 60243-1 17 |
| Dielectric Constant (23°C) | 3.10 - 3.90 | ASTM D150 | |
| Dissipation Factor (23°C) | 0.044 - 0.048 | ASTM D150 | |
| Comparative Tracking Index | 596 | IEC 60112 18 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 24 | % | ISO 4589-2 19 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.3 - 80.0 | °C | |
| Drying Time | 3.9 - 12 | hr |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 11This information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | 10 °C/min |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 16 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 17 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 18 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 19 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Acrigel® ECL | Unigel Plásticos | Acrylic (PMMA) | Acrigel® |
| ALCUDIA® EBA CA-3230B | REPSOL | EBA | ALCUDIA® EBA |
| Machine Cast MC-70 A/B | BJB Enterprises, Inc. | TSU | Machine Cast |
| NHU-PPS 21901C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |
| POCAN® B 5220 XF 000000 | LANXESS GmbH | PBT | POCAN® |