Sarlink® TPE EE-1240N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqhAfX_Sarlink-TPE-EE-1240N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE EE-1240N is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Sarlink®The main characteristics of TPE EE-1240N are: low hardness. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 45 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 42 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 40 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 0.690 | MPa | ISO 37 |
| Flow : 100% strain | 1.15 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 5.40 | MPa | ISO 37 |
| Flow : Fracture | 3.40 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 890 | % | ISO 37 |
| Flow : Fracture | 660 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 15 | kN/m | ISO 34-1 |
| Flow | 19 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 11 | % | ISO 815 |
| 70°C, 22 hr | 28 | % | ISO 815 |
| 90°C, 70 hr | 56 | % | ISO 815 |
| 125°C, 70 hr | 76 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | 30 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 47 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 7.3 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | -3.5 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | 39 | % | ISO 188 |
| Flow : 125°C, 168 hr | 56 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | 12 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | -3.5 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -1.1 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 20 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | 3.0 | % | ISO 188 |
| Flow : 125°C, 168 hr | 27 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Support a, 110°C, 1008 hr 8 | 2.2 | ISO 188 | |
| Support a, 110°C, 1008 hr 9 | 3.3 | ISO 188 | |
| Support a, 110°C, 1008 hr 10 | 4.0 | ISO 188 | |
| Support a, 125°C, 168 hr 11 | 0.20 | ISO 188 | |
| Support a, 125°C, 168 hr 12 | 0.60 | ISO 188 | |
| Support a, 125°C, 168 hr 13 | 0.90 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 258 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 1 sec |
| 9 . | 5 sec |
| 10 . | 15 sec |
| 11 . | 1 sec |
| 12 . | 5 sec |
| 13 . | 15 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melos™ FM 976 | Melos GmbH | EPM | Melos™ |
| RTP 100 MF GB 20 UV | RTP Company | PP, Unspecified | RTP |
| Daplen™ ED306UBB | Borealis AG | TPO | Daplen™ |
| LUVOCOM® 1-8841 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| TECHNYL® C 52G3 MZ25 GREY R7035 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |