LNP™ LUBRILOY™ Z20001 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqggOZ_LNP-LUBRILOY-Z20001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY Z20001 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant. Also known as: LNP* LUBRILOY* Compound Z-FR Product reorder name: Z20001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.80 to 1.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.12 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2120 | MPa | ASTM D638 |
| -- | 2010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/5 |
| Break 3 | 48.0 | MPa | ASTM D638 |
| Break | 49.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/5 |
| Break 5 | 40 | % | ASTM D638 |
| Break | 24 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2130 | MPa | ASTM D790 |
| -- 7 | 1930 | MPa | ISO 178 |
| Flexural Stress | 74.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.27 | ||
| vs. Itself - Static | 0.19 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 54.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 420 | J/m | ASTM D256 |
| 23°C 8 | 31 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2100 | J/m | ASTM D4812 |
| 23°C 9 | 210 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 46.0 | J | ASTM D3763 |
| -- | 45.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 120 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 116 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 105 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 99.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.8E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 277 to 293 | °C | |
| Mold Temperature | 60.0 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ S895 | Miracll Chemicals Co., Ltd. | TPU-Polyether | Mirathane™ |
| NEFTEKHIM PP 1502H (S30S) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Aarolene® AVPS GP 100-1 | Aaron Industries Corp. | PS (GPPS) | Aarolene® |
| Daplen™ EF150HP | Borealis AG | TPO | Daplen™ |
| Fiberfil® PP-60/TC/40 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |