COSMOPLENE® FL7015E2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqagI4_COSMOPLENE-FL7015E2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| COSMOPLENE FL7015E2 is Polypropylene Homopolymer designed for cast film with good flow compatibility when coextruded with selected Copolymer/Terpolymer as skin layer. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 800 | % | ASTM D638 |
| Apparent Bending Modulus | 1420 | MPa | ASTM D747 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| secant modulus | Internal method | ||
| MD | 740 | MPa | Internal method |
| TD | 760 | MPa | Internal method |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 165 | °C |
| Additional Information |
|---|
| Resin Temperature: 250°CChill Roll Temperature: 26°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 35195 | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Adiprene® Duracast® E900 | Chemtura | PUR-Ether/MDI | Adiprene® Duracast® |
| ALTECH® PA66 A 4240/500 GF15 MR25 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Karina IVORY PVC COMPOUND HML-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ASPIRE VINYL™ G800 | Axiall Corporation | PVC, Flexible | ASPIRE VINYL™ |