Bayblend® T85 SG
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqVR6i_Bayblend-T85-SG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ABS) blend; unreinforced; injection molding grade; Vicat/B 120 temperature = 130 °C; high melt flow; suitable for DirectCoating / DirectSkinning. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 260°C, 3.00 mm | 0.55 to 0.75 | % | |
| Flow : 260°C, 3.00 mm | 0.55 to 0.75 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.60 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield, 23°C | 55.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 54.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield, 23°C | 4.9 | % | ISO 527-2/50 |
| Break, 23°C | > 50 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 52.0 | J | |
| 23°C | 46.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 128 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 108 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 129 | °C | ISO 306/B50 |
| -- | 130 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.5E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.00 | ||
| 23°C, 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 2.5E-3 | ||
| 23°C, 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index (Solution A) | 200 | V | IEC 60112 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2(260°C) | 255 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 80°C MT, 500 bar |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1521AH | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Sylvin 86023-38DUV White 1529 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Hax™ CAT 100 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Kepital® F20-03 M | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| I. Stern SH432HG | I. STERN & CO. INC. | PS (HIPS) | I. Stern |