FLEXITEQ™ F80A590
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | FLEXITEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gq96d9_FLEXITEQ-F80A590.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FLEXITEQ™ F80A590 is a flame retardant material developed based on Santoprene™ rubber technology. It is designed to provide excellent flame retardancy to meet the required Oxygen Index test whilst retaining the usual benefits of the Santoprene material providing outstanding properties including soft-touch, good colourability and good mouldability. FLEXITEQ™ F80A590 is developed for extrusion applications. It has good process thermal stability owing to very stable flame retardant system which complies with the European RoHS requirement. Note: The letters "UV" or "W" indicate additional UV stabilisation [ ie: FLEXITEQ™ F80A590UV ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 82 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 3.00 | MPa | ASTM D412 |
| Tensile Strength 2(Break) | 3.90 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 300 | % | ASTM D412 |
| Tear Strength 4(23°C) | 27.0 | kN/m | ASTM D624 |
| Compression Set 5(23°C, 70 hr) | 46 | % | ASTM D395B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 160 to 190 | °C | |
| Cylinder Zone 2 Temp. | 180 to 210 | °C | |
| Cylinder Zone 3 Temp. | 180 to 210 | °C | |
| Cylinder Zone 4 Temp. | 180 to 210 | °C | |
| Cylinder Zone 5 Temp. | 180 to 210 | °C | |
| Melt Temperature | 180 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Die C, 500 mm/min |
| 2 . | Die C, 500 mm/min |
| 3 . | Die C, 500 mm/min |
| 4 . | Die C, 500 mm/min |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2720 M210 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| 3M™ Dyneon™ Fluoroplastic PVDF 60100000 | 3M Advanced Materials Division | PVDF | 3M™ Dyneon™ Fluoroplastic |
| Hostacom ERC 361N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Kareline® ABMS6040 | Plasthill Oy | ABS | Kareline® |
| Rotuba CAP CP800 (18% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |