LAMIGAMID® 309
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Schwartz Technical Plastic |
| Trademark: | LAMIGAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gpUeOE_LAMIGAMID-309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Oil filled Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.0 | -- | % | ISO 62 |
| Saturated, 23°C | 4.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 130 | 110 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2900 | 2300 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 75.0 | 55.0 | MPa | ISO 527-2 |
| Fracture | 110 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 30 | -- | % | ISO 527-2 |
| Flexural Modulus | 2700 | 2100 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D1894 | |||
| With steel-dynamic | 0.040 | 0.080 | ASTM D1894 | |
| With steel-static | 0.14 | 0.20 | ASTM D1894 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | > 6.0 | > 18 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | No Break | No Break | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 110 | -- | °C | ISO 75-2/A |
| Melting Temperature | 200 - 220 | -- | °C | |
| CLTE - Flow (20 to 100°C) | 7.0E-5 - 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1670 | -- | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.25 | -- | W/m/K | ISO 8302 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Dielectric Strength | 50 | 20 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.70 | -- | IEC 60250 | |
| Dissipation Factor | 0.030 | -- | IEC 60250 |
| Additional Information |
|---|
| 干燥 Creep Rate Stress, DIN 53444, 1% Elongation: >15 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >20 N/mm²Friction Wear: 0.06 µm/KmPenetration Resistance, DIN 53482: 1E15 ohm-cmCreepage/leakage Resistance: KA3cThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: -40°C |
| 调节后的 Creep Rate Stress, DIN 53444, 1% Elongation: >8 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >12 N/mm²Friction Wear: 0.06 µm/KmPenetration Resistance, DIN 53482: 1E12 ohm-cmCreepage/leakage Resistance: KA3bThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: 120°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAFIN™ PB50GM | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| TAIRIPRO K4535 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| VECTRA® J540 | Celanese Corporation | LCP | VECTRA® |
| Nymax™ 1308 A HS Black 13 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Axiall PVC 12850 | Axiall Corporation | PVC, Flexible | Axiall PVC |