megol® CA 63 SV/P/FCX1
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | API SpA |
| Trademark: | megol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gpQAtv_megol-CA-63-SV-P-FCX1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
megol® CA 63 SV/P/FCX1 is a Styrene Ethylene Butylene Styrene Block Copolymer (SEBS) product. It can be processed by calendering and is available in Europe. Applications of megol® CA 63 SV/P/FCX1 include conveyors, fabrics/fibers, food contact applications and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 10.0 | MPa | |
| 100% Strain | 3.10 | MPa | |
| 300% Strain | 5.40 | MPa | |
| Tensile Elongation (Break) | 640 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 49.0 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 | hr |
| Note Message | |
|---|---|
| 1 . | Without Notch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8533 | Colorite Polymers | PVC, Unspecified | Unichem |
| Cadence™ ADD2 | Eastman Chemical Company | Copolyester | Cadence™ |
| Ferro PP LPP40BK69HB-BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| ARLEN™ C230N | Mitsui Chemicals America, Inc. | Nylon 6T | ARLEN™ |
| API II 550-HF | API II, Inc. | PS (HIPS) | API II |