ExxonMobil™ PP5341E1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gpP6k5_ExxonMobil-PP5341E1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A homopolymer resin with low melt flow rate has high melt strength and softening resistance at high temperatures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.83 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 13 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | |||
| -- 3 | 1190 | MPa | ASTM D790A |
| -- 4 | 1390 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 52 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 83.7 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 51.9 | °C | ASTM D648 |
| Legal statement |
|---|
| 未经埃克森美孚化工书面允许，这种产品包括其产品名称，不得在任何医疗应用领域予以使用或有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 700 GB 40 | RTP Company | HDPE | RTP |
| Arak LLDPE HD6070EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| Ketron® PEEK-HPV | Quadrant Engineering Plastic Products | PEEK | Ketron® |
| Idemitsu PS NS-100 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| Jamplast EX-02 PC | Jamplast, Inc. | PC | Jamplast |