LNP™ LUBRICOMP™ DL003EU compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | goyni7_LNP-LUBRICOMP-DL003EU-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DL003EU is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Easy Molding, UV Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DL-4030 EM UV Product reorder name: DL003EU |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.29 | g/cm³ | ISO 1183 |
| -- | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.80 to 0.90 | % | |
| Across Flow : 24 hr | 0.80 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2190 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 45.1 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2 |
| Break | 50.3 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.6 | % | ASTM D638 |
| Yield | 5.5 | % | ISO 527-2 |
| Break | 26 | % | ASTM D638 |
| Break | 9.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2310 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.5 | MPa | ASTM D790 |
| -- | 84.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.18 | ||
| vs. Itself - Static | 0.070 | ||
| Wear Factor - Washer | 60.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2100 | J/m | ASTM D4812 |
| 23°C 3 | 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 117 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 128 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-IM2G13 | Polymer Resources Ltd. | Nylon 66 | PRL |
| AQUAFORCE® PA66 G50-01 SCHWARZ | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | AQUAFORCE® |
| Geon™ Vinyl Flexible R355AM | PolyOne Corporation | PVC+NBR | Geon™ Vinyl Flexible |
| Knorstan™ 4030R30 Bk-1 | Technical Polymers, LLC | PPE+PS | Knorstan™ |
| HIPTEN® 15080 | HIP-PetroHemija | LDPE | HIPTEN® |