TECHNYL® B 50H1 NATURAL L
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | goxLbF_TECHNYL-B-50H1-NATURAL-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® B 50H1 Natural L is an unreinforced melamine cyanurate flame retarded copolyamide 66/6. This product has been heat stabilised and is suitable for injection moulding. This product is available in natural and other colors upon request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 1.1 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.10 | -- | Internal Method |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Fire and Smoke F Index | I2/F3 | -- | NF F16-101 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3600 | 2200 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Yield | 85.0 | -- | MPa | ASTM D638 |
| Yield | 80.0 | 40.0 | MPa | ISO 527-2/1A |
| Break | 70.0 | 40.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ||||
| Yield | 4.0 | 5.0 | % | ISO 527-2/1A |
| Break | 10 | -- | % | ASTM D638 |
| Break | 10 | 100 | % | ISO 527-2/1A |
| Flexural Modulus | 3650 | -- | MPa | ASTM D790 |
| Flexural Strength | 120 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 kJ/m² | No Break | ISO 179/1eU | |
| Notched Izod Impact | ||||
| 23°C | 60 | -- | J/m | ASTM D256 |
| 23°C | 5.0 | 6.5 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 242 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 6.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.60 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.060 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 575 | 600 | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.380 mm | V-0 | -- | ||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 33 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 245 to 255 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8299-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Allen ABS 556/499 | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| Hyundai EP PA66 LD280 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| LCA® N6-33GF | UniPlas, Inc. | Nylon 6 | LCA® |
| Lumid® HI2152A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |