Leona™ 14G33
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | goUYAm_Leona-14G33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 14G33 is a Polyamide 66 (Nylon 66) product filled with 33% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 14G33 include automotive, electrical/electronic applications and engineering/industrial parts. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.7 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.7 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 96 | 75 | ||
| R-Scale | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9800 | 7800 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 208 | 143 | MPa | ISO 527-2 |
| -- | 210 | 135 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 3.0 | 5.0 | % | ASTM D638 |
| Break, 23°C | 4.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 10400 | 6300 | MPa | ASTM D790 |
| 23°C | 9600 | 6700 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 325 | 210 | MPa | ASTM D790 |
| 23°C | 302 | 213 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 15.0 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 13 | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 90 | 97 | kJ/m² | ISO 179 |
| Notched Izod Impact | 130 | 170 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.30 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 33 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 425 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HP132 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Shinko-Lac® ASA TW35 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| AKROMID® A3 ICF 15 black (5056) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Daplen™ EE188AI | Borealis AG | PP, Unspecified | Daplen™ |
| Eltex® A5006PFN1281 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |