Arnitel® PL650
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gnqy6T_Arnitel-PL650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnitel® PL650 is a Thermoplastic Copolyester Elastomer (TPC-ET) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Arnitel® PL650: Flame Rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 26.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 430 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 35.0 | MPa | |
| 5.0% Strain | 17.1 | MPa | |
| 10% Strain | 22.1 | MPa | |
| 50% Strain | 22.9 | MPa | |
| 100% Strain | 22.1 | MPa | |
| Nominal Tensile Strain at Break | 370 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 23 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 21 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 221 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-72D-B30 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| SLOVAMID® 6 BT LS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| VESTAKEEP® 5000G | Evonik Industries AG | PEEK | VESTAKEEP® |
| Vinnolit® SA 1062/7 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Karina GRAY PVC COMPOUND 105900-18/121-B-ACE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |