VESTAMID® D DX9304
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® D |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gnRww0_VESTAMID-D-DX9304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characterization: impact-resistant, heat- and light-stabilized Applications: tubing systems subjected to higher temperatures, e.g., hydraulic clutch lines Its advantages over PA 12 exhibit in the
The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.04 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 2.2 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.7 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1800 | 1200 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 50.0 | 41.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 5.0 | 20 | % | |
| Break | > 50 | > 50 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C, Complete Break | 30 | 18 | kJ/m² | |
| 23°C, Partial Break | 50 | 95 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed 2 | 175 | -- | °C | ISO 75-2/B |
| 0.45 MPa, Unannealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed 3 | 55.0 | -- | °C | ISO 75-2/A |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 175 | -- | °C | ISO 306/B |
| Melting Temperature 4 | 213 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.5E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 24 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.10 | -- | ||
| 1 MHz | 3.20 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.056 | -- | ||
| 1 MHz | 0.031 | -- | ||
| Comparative Tracking Index 5(Solution A) | > 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Electrolytical Corrosion | AN 1,2 | -- | IEC 60426 | |
| ISO Shortname | PA612-HI, EHL, 18-020 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | measured at specimen 60x60x2mm |
| 2 . | after conditioning at 180 °C / 60 min |
| 3 . | after conditioning at 180 °C / 60 min |
| 4 . | 2nd Heating |
| 5 . | 50 drops Value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L HPT-1 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| VICTREX® PEEK 150CA30 | Victrex plc | PEEK | VICTREX® PEEK |
| Hifax CB 1128 A/1 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Karina IVORY PVC COMPOUND 750-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 01508 (Injection) | Plastics Engineering Co. | Polyester, TS | Plenco |