PRL TP-HG40
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gnDGgk_PRL-TP-HG40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRL TP-HG40 is a Polybutylene Terephthalate (PBT) product filled with 40% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 25 to 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 138 | MPa | |
| Break, 3.18 mm | 138 | MPa | |
| Flexural Modulus (3.18 mm) | 10300 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 216 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 193 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 5006 | SILON s.ro | PP, Unspecified | TABOND |
| T-Blend® 4792N-NB | TSRC Corporation | TPE | T-Blend® |
| Niretan A F20 | Soredi S.p.a. | Nylon 66 | Niretan A |
| NuSil EPM-2410 | NuSil Technology | Silicone | NuSil |
| Latamid 66 E21 G/30 | LATI S.p.A. | Nylon 66 | Latamid |