Jamplast JPEVA10
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gmed0F_Jamplast-JPEVA10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JPEVA10 is an EVA copolymer with good toughness, flexibility and clarity. Applications include laminating and heavy duty films as well as injection and blow molding. JPEVA10 contains no additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 10.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 94 | ||
| Shore D | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 13.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 700 | % | ASTM D638 |
| Flexural Modulus | 79.3 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 84.8 | MPa | |
| 1% Secant, TD | 91.0 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 6.23 | MPa | |
| TD : Yield | 5.81 | MPa | |
| MD : Break | 25.9 | MPa | |
| TD : Break | 18.9 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 350 | % | |
| TD : Break | 500 | % | |
| Dart Drop Impact (51 µm) | 400 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 221 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 510 mm/min |
| 2 . | Type IV, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trexprene® A64BI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| APEX® 3701-60NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| GAPEX® RPP30EB44BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| Deprene 253-50 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |
| 3M™ Dyneon™ PTFE Compound TF R4215 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |