LNP™ STAT-KON™ ZE004 compound
| Category: | Polyphenylene, Unspecified , Polyphenylene |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gmXUrP_LNP-STAT-KON-ZE004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON ZE004 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber. Also known as: LNP* STAT-KON* Compound ZC-1004 Product reorder name: ZE004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.53 | % | ISO 294-4 |
| Flow : 24 hr | 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 24800 | MPa | ASTM D638 |
| -- | 14700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 80.7 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2 |
| Break | 104 | MPa | ASTM D638 |
| Break | 103 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 0.50 | % | ASTM D638 |
| Break | 0.96 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 24100 | MPa | ASTM D790 |
| -- | 12700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 151 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D4812 |
| 23°C 3 | 18 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 139 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 135 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7-7015R | Spartech Polycom | PC | Spartech |
| Vibrathane® 8585 | Chemtura | PUR-Ester/MDI | Vibrathane® |
| Nylfor® A2 FR1/2A NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Aarolene® ARPS 100-2 | Aaron Industries Corp. | PS (MIPS) | Aarolene® |
| Lumid® HI3232A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |