| Starglas GX061104 is a PSU resin (also known as Starglas PSU A 3/4) |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 73.0 | MPa | |
| Break | 53.0 | MPa | |
| Tensile Strain (Yield) | 5.9 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2600 | MPa | ISO 178 |
| Flexural Stress | 113 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 151 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 310 to 330 | °C | |
| Middle Temperature | 310 to 330 | °C | |
| Front Temperature | 310 to 330 | °C | |
| Processing (Melt) Temp | 310 to 330 | °C | |
| Mold Temperature | 150 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPOLEN® FD 243-51 | MOL Petrochemicals Co. Ltd. | LDPE | TIPOLEN® |
| NOVAREX® 7030R | Mitsubishi Engineering-Plastics Corp | PC | NOVAREX® |
| KRALASTIC® AN-450 | Nippon A&L Inc. | ABS | KRALASTIC® |
| Karina CLEAR PVC COMPOUND -E 85/209-D-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8980-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |