Centrex® 833A
| Category: | ASA+AES , Acrylonitrile Styrene Acrylate + AES |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Centrex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | glqB4c_Centrex-833A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Centrex®833A is an acrylonitrile-styrene-acrylate AES (ASA AES) product,. It can be processed by co-extrusion molding, extrusion, thermoforming or profile extrusion molding, and is available in North America. Centrex®The application areas of 833A include sporting goods, thin plates, marine applications and outdoor applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 10 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 1.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2030 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 35.2 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 2.4 | % | ASTM D638 |
| Flexural Modulus - Tangent 4 | 1720 | MPa | ASTM D790 |
| Flexural Strength 5 | 35.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 130 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 150 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 70.5 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -40 to 40°C | 1.7E-4 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60 °, high-gloss surface, no texture) | 90 - 100 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Melt Temperature | 210 - 241 | °C | |
| Die Temperature | 210 - 241 | °C |
| Extrusion instructions |
|---|
| Recommended Regrind: up to 40%Polish roll Top: Down stack 200°F, Up stack 200°FPolish roll Middle: Down stack 165°F, Up stack 190°FPolish roll Bottom: Down stack 200°F, Up stack 180°F |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 5.1 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene GPP1615/2 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Sumitomo Epoxy E 264H | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| NYLOY® MG-4033N | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| ASTALON™ S2000U | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Jampilen HP529J | Jam Polypropylene Company | PP Homopolymer | Jampilen |