AFFINITY™ PF 1146G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | glngWh_AFFINITY-PF-1146G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AFFINITY* PF 1146 Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is designed for high speed packaging applications requiring low seal initiation temperature and good machinability (low consistent coefficient of friction and low block force). This resin is designed to give a COF of < 0.2 for an ~1.0 mil sealant layer in a coextruded film, and to run fast and trouble-free on most extrusion equipment, including blown film dies equipped with narrow die gaps.
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.899 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy (51 µm) | 3.56 | J | Internal method |
| Film Puncture Force (51 µm) | 48.9 | N | Internal method |
| Film Puncture Resistance (51 µm) | 9.60 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 51.2 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 55.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 6.43 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 5.98 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 37.3 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 42.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 550 | % | ASTM D882 |
| TD : Fracture, 51 µm | 600 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 380 | g | ASTM D1922 |
| TD : 51 µm | 460 | g | ASTM D1922 |
| Seal Initiation Temperature 1(51 µm) | 75.0 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 78.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 95.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 77 | ASTM D2457 | |
| Clarity 2(50.8 µm) | 90.0 | ASTM D1746 | |
| Haze (50.8 µm) | 5.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 221 - 232 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆类型：改良 LDPE 或中等工作阻隔 模具间隙：70 密尔 (1.8 mm) 熔体温度：430-450°F (221-232°C) 放大比：2.5:1 |
| Note Message | |
|---|---|
| 1 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed on Instron tensiometer 10 inches/minute (250 mm/s). |
| 2 . | The ASTM method is under development. BYK-Gardner-Hazeguard has been utilized. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5410UV D84 | Spartech Polycom | PP, Unspecified | Spartech |
| ACCUTECH™ HP0339C20L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| BLUESTAR® 1100A | Nantong Xingchen Synthetic Material Co., Ltd. | PBT | BLUESTAR® |
| KumhoSunny PBT/ABS HAB8750 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| Lucky Enpla LGF3300 | Lucky Enpla Co LTD | PBT | Lucky Enpla |