Nypel® RC6024 BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Nypel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gleGPK_Nypel-RC6024-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nypel RC6024 BK is a semi crystalline, heat stabilized, low viscosity, 30% mineral and glass fiber reinforced black injection molding compound produced with at least 20% recycled PA6 feedstocks. It possesses a balance of engineering properties in combination with excellent dimensional stability, good flow and processability, low warp and good chemical, abrasion and sink-mark formation resistance. This product is a regional grade available in North America only. Applications Nypel RC6024 BK is generally recommended for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, engine covers and shrouds. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.2 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 3.8 | kJ/m² | |
| 23°C | 4.2 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G25 272 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| TECHNYL® A 218 V35 BLACK 34 NG | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| ADDILENE H 140 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Karina WHITE PVC COMPOUND 750D10/120-IS-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kepital® FB2025 | KEP Americas | Acetal (POM) Copolymer | Kepital® |