Order Products : sales@su-jiao.com
Laticonther 62 CPG/750
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laticonther |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | glRxpu_Laticonther-62-CPG-750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High thermal conductivity product based on Polyamide 6 (PA 6). Special filler. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.40 to 0.60 | % | |
| Flow : 2.00 mm | 0.35 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 90.0 | °C | |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 1.7 | W/m/K | ASTM E1952-01 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | > 3.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 | RTP Company | PP, Unspecified | RTP |
| RTP 1000 TFE 15 | RTP Company | PBT | RTP |
| TAIRIPRO K9010 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Enviramid® N2350HL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| LNP™ THERMOCOMP™ RF00CSXP compound | SABIC Innovative Plastics Europe | Nylon, Unspecified | LNP™ THERMOCOMP™ |