ASTADUR™ B4300G6-UV
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTADUR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | glR6IY_ASTADUR-B4300G6-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTADUR™ B4300G6 is a 30% glass fibre reinforced, UV stabilized grade of polybutylene terephthalate (PBT) polymer. It has excellent processability, high rigidity and heat resistance and is resistant to chemical attack. It is suitable for applications where rigidity and heat resistance are of high importance. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTADUR™ B4300G6UV ]. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 125 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 6800 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 220 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 215 | °C | ASTM D648 |
| Vicat Softening Temperature | 220 | °C | ASTM D1525 5 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 230 - 240 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 90.0 | °C | |
| Injection Pressure | 60.0 - 140 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.300 - 1.00 | MPa | |
| Clamp Tonnage | 4.0 - 8.0 | kN/cm² |
| Injection instructions |
|---|
| Screw Speed: Minimum |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Norylux™ 30% GF | Westlake Plastics Company | PPE+PS | Norylux™ |
| Ferro PP TPP20AC06HB | Ferro Corporation | PP Homopolymer | Ferro PP |
| LAPEROS® S475 | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| LEXAN™ FXG1413T resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Petrotene® PP A3 G30 PRTA011 PH360 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |