Ebalta AH 110 / TGS
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gl9egP_Ebalta-AH-110-TGS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AH 110 is a non-filled epoxy resin with high strength and dimensional stability, even at increasing temperature. It also can be used as casting resin with powder fillers as aluminium powder, as laminating resin with glass fabrics and as binding resin with granular fillers as aluminium granules. Depending on the application if just needs to use a different hardener for the mixture. As laminating resin AH 110 / TGS is suitable for thin high solid laminates. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 83 to 89 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3000 to 3600 | MPa | ISO 178 |
| Flexural Stress | 118 to 138 | MPa | ISO 178 |
| Compressive Stress | 100 to 120 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 12 to 28 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 96.0 to 102 | °C | ISO 75-2/B |
| Glass Transition Temperature | 97.0 | °C | DSC |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 22 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time (80°C) | 12 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.11 to 1.15 | g/cm³ | |
| Viscosity (25°C) | 1.1 to 1.5 | Pa·s | |
| Curing Time (20°C) | 6.0 to 8.0 | hr | |
| Pot Life 1(20°C) | 20 to 25 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 246SI V30 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| ALCOM® ABS 530/29 BL1241-07MCF | ALBIS PLASTIC GmbH | ABS | ALCOM® ABS |
| EMPILON® 530 | EMPILON | SEBS | EMPILON® |
| EPIMIX PBT GFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| Hanwha Total PP TB70W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |