CYCOLOY™ C2950 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gl5lWq_CYCOLOYC2950resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 116 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture | 45.0 | MPa | ISO 527-2/5 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 4.0 | % | ISO 527-2/5, ISO 527-2/50 |
| Fracture | 65 | % | ISO 527-2/5 |
| Fracture | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2700 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 54.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | No Break No Break | ISO 179/1eU | |
| 23°C | No Break No Break | ISO 179/1eU | |
| Notched Izod Impact 5 | ISO 180/1A | ||
| -30°C | 14 | kJ/m² | ISO 180/1A |
| 23°C | 44 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 100 mm span | 103 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 90.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 118 | °C | ISO 306/A50 |
| -- | 110 | °C | ISO 306/B50 |
| -- | 112 | °C | ISO 306/B120 |
| Ball Pressure Test (100°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 60°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI | 85.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | IEC 60250 | |
| 60 Hz | 2.80 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 4.0E-3 | IEC 60250 | |
| 60 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 6.0E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | 5VB | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 210 - 240 | °C | |
| Middle Temperature | 230 - 270 | °C | |
| Front Temperature | 240 - 280 | °C | |
| Nozzle Temperature | 230 - 270 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2283 HF TFE 10 | RTP Company | PEEK | RTP |
| Derakane® 510N | Ashland Performance Materials | Vinyl Ester | Derakane® |
| FORMOCON® FM090 | Formosa Plastics Corporation | Acetal (POM) Copolymer | FORMOCON® |
| LNP™ LUBRICOMP™ MFL36S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |
| MAJORIS EW251 - 7818/5 | AD majoris | PP, Unspecified | MAJORIS |