TAIRIREX GP5500
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRIREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gkSERw_TAIRIREX-GP5500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC PS resin GP5500 meets the requirements of UL, SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.5 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 51.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 3330 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| 23°C | 98.1 | MPa | ASTM D790 |
| 23°C | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 18 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(1.8 MPa, Annealed, 3.18 mm) | 95.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 104 | °C | ASTM D1525, ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Natural Color) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Residual Monomer | < 700 | ppm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Hopper Temperature | 40.0 | °C | |
| Rear Temperature | 195 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 220 | °C | |
| Nozzle Temperature | 215 | °C | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 80°Cx2Hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Catalyst PS/2 Black | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| FORMULA P COMP 3240 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| HiFill® PP GF20 CC HS | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| KOPLA PA66 KDE1030 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| POLYCOMPO PE 20200J | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |