Zhongfa PA66 ST-12
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Yuyao Zhongfa Engineering Plastics Co. Ltd. |
| Trademark: | Zhongfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gkPkgm_Zhongfa-PA66-ST-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zhongfa PA66 ST-12 is a polyamide 66 (nylon 66) material,. This product is available in the Asia-Pacific region and is processed by injection molding. The main characteristics of Zhongfa PA66 ST-12 are: impact resistance. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 57.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus | 1050 | MPa | ASTM D790 |
| Flexural Strength | 75.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 72.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 19 kJ/m² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 6.0 - 8.0 | hr | |
| Processing (Melt) Temp | 235 - 265 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 60.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1022HS | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Reny® NXG5050NF | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| EXCELLOY CK50 | Techno Polymer Co, Ltd. | PC+ABS | EXCELLOY |
| Polimid A 25 GF V0F | Poliblend S.p.a. | Nylon 66 | Polimid A |
| Sylvin 5145-70 Red 6193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |