Premi-Glas® 1200H-10

Category:	TS, Unspecified , Thermoset, Unspecified
Manufacturer:	Premix, Inc.
Trademark:	Premi-Glas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gkNQxq_Premi-Glas-1200H-10.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Premi-Glas® 1200H-10 is a fiberglass reinforced thermoset sheet molding compound for general purpose applications requiring thermal stability and stiffness.

Key Features and Benefits:

Good dimensional stability, including excellent thermal resistance.

Pigmentable for molded-in color; best appearance with mold texture.

Excellent property retention in cold and hot environments.

Suitable for outdoor use in applications involving UV exposure and water immersion in accordance with UL746C (f1), see File E42524

General Information
Filler / Reinforcement	Glass Fiber
Features	Good Corrosion Resistance Good Dimensional Stability Good Thermal Stability High Stiffness
Uses	General Purpose Outdoor Applications
UL File Number	E42524
Forms	SMC - Sheet Molding Compound

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.70 to 1.85	g/cm³
Molding Shrinkage - Flow	0.20 to 0.35	%
Outdoor Suitability	f1		UL 746C

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	11000	MPa	ASTM D638
Tensile Strength (Compression Molded)	20.7	MPa	ASTM D638
Flexural Modulus (Compression Molded)	9650	MPa	ASTM D790
Flexural Strength (Compression Molded)	68.9	MPa	ASTM D790
Compressive Strength ¹	121	MPa	ASTM D695
Poisson's Ratio	0.30

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	310	J/m	ASTM D256
Unnotched Izod Impact (Compression Molded)	360	J/m	ASTM D4812

Thermal	Nominal Value	Unit	Test Method
CLTE
Flow	2.5E-5	cm/cm/°C
Transverse	3.5E-5	cm/cm/°C
Thermal Conductivity	0.30	W/m/K
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI Str	130	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	15	kV/mm	ASTM D149
Arc Resistance	180	sec	ASTM D495

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.52 mm)	HB		UL 94

Injection	Nominal Value	Unit
Mold Temperature	149	°C
Injection Pressure	3.45 to 6.89	MPa

Note Message
1 .	Compression Molded

Resin Grade	Manufacturer	Category	Trademark
Teldene® H03BPM	National Petrochemical Industries Company (NATPET)	PP Homopolymer	Teldene®
Etinox® ER-C130	Ercros, S.A.	PVC, Rigid	Etinox®
Elastamax™ XL 0135-33	PolyOne Corporation	SBC	Elastamax™
EL-Lene™ M3204RU	SCG Chemicals Co., Ltd.	LLDPE	EL-Lene™
EnviroPro 3010GM	West Michigan Compounding	PP Homopolymer	EnviroPro