MAJORIS BW260 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gkC4Xl_MAJORIS-BW260---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BW260 - 8229 is a 20% glass - filled polypropylene compound intended for injection moulding. The product is available in both black (BW260 - 8229) and natural (BW260) but other colours can be provided on request. BW260 - 8229 has been developed especially for the automotive applications and electrical components. BW260 - 8229 makes it very easy to process even for complicated parts with long flow paths and it offers very high productivity with short cycle times. BW260 - 8229 is formulated to give an excellent surface finish. APPLICATION Products requiring good rigidity, low shrinkage, high dimensional stability can suitably be made from BW260 - 8229. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.0 - 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 55 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1070 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 120 | % | ISO 527-2 |
| Flexural Modulus 1 | 1100 | MPa | ISO 178 |
| Flexural Stress 2 | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 104 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1800 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| ELASTOSIL® FLR 3905/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® FLR |
| Huafon HF-1095A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Hostacom TKC 270N D72253 | LyondellBasell Industries | PP Copolymer | Hostacom |
| ORTHTEK® WF | Greene, Tweed & Co. | PEEK | ORTHTEK® |