HIPTEN® 22007 A17
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPTEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | giux7O_HIPTEN-22007-A17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HIPTEN® 22007A17 is low density polyethylene resin developed for production of shrink film,carrier bags. HIPTEN® 22007A17 has outstanding mechanical properties, very good processability and homogeneous appearance and good heat welding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 10.0 | MPa | ISO 527-2 |
| Fracture | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 650 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| TD : Yield, 40 µm | 11.0 | MPa | ISO 527-3 |
| MD : Break, 40 µm | 24.0 | MPa | ISO 527-3 |
| TD : Break, 40 µm | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture | 350 | % | ISO 527-3 |
| TD : Fracture | 600 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 150 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40.0 µm | 135.1 | kN/m | ASTM D1922 |
| TD : 40.0 µm | 173.7 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 200 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ablebond 958-11 | Henkel Ablestik | Epoxy | Ablebond |
| Fainplast PVC PM 8005 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Kumho EP HAC 8270 | Korea Kumho Petrochemical Co., Ltd. | PC+ABS | Kumho EP |
| KOPA® KN333G25 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| LNP™ LUBRICOMP™ DL002 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |