QR Resin QR-9006-GF40
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | giOSFC_QR-Resin-QR-9006-GF40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
QR Resin QR-9006-GF40 is a Polyamide 6 (Nylon 6) product filled with 40% glass fiber. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 152 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 9510 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 241 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| Melting Temperature | 216 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 4.0 | hr | |
| Rear Temperature | 232 to 288 | °C | |
| Middle Temperature | 232 to 288 | °C | |
| Front Temperature | 232 to 288 | °C | |
| Nozzle Temperature | 232 to 288 | °C | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® 1082V | Zeon Chemicals L.P. | NBR | Nipol® |
| Grilon® BZ 1/2 | EMS-GRIVORY | Nylon 6 | Grilon® |
| Keltan® 2660 | LANXESS Buna GmbH | EPDM | Keltan® |
| IPC PP 4820C-GF Black | International Polymers Corporation | PP, Unspecified | IPC PP |
| Leona™ 91G40 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |