LNP™ LUBRICOMP™ RX85514 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | giGaS1_LNP-LUBRICOMP-RX85514-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-R-85514 Product reorder name: RX85514 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.61 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.93 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3700 | MPa | ASTM D638 |
| -- | 3820 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 79.0 | MPa | ASTM D638 |
| Break | 78.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 7.4 | % | ISO 527-2/5 |
| Break 3 | 7.3 | % | ASTM D638 |
| Break | 7.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3320 | MPa | ASTM D790 |
| -- 5 | 3560 | MPa | ISO 178 |
| Flexural Stress | 109 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.39 | ||
| vs. Itself - Static | 0.34 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.0500 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 3.50 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 6 | 4.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 520 | J/m | ASTM D4812 |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.10 | J | ASTM D3763 |
| -- | 1.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 247 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 7 | 228 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 117 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 8 | 112 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8150C | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| AKROMID® A3 1 L natural (4800) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| Echo® RPH20TC BK | Ravago Manufacturing Americas, LLC | PP Homopolymer | Echo® |
| ELASTOSIL® R plus 4020/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| OmniCarb™ PC/PBT 1420 CTI | OMNI Plastics, LLC | PC+PBT | OmniCarb™ |