Matrixx F663E33
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | The Matrixx Group, Inc. |
| Trademark: | Matrixx |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | giBMBh_Matrixx-F663E33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Matrixx F663E33 is a polyamide 66 (nylon 66) material, which contains a 33% glass fiber reinforced material. This product is available in North America and is processed by injection molding. The main characteristics of Matrixx F663E33 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 - 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 190 | MPa | ASTM D638 |
| Flexural Modulus - Tangent | 8620 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 249 | °C | ASTM D648 |
| RTI | 65.6 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 93.3 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 271 - 299 | °C | |
| Middle Temperature | 271 - 299 | °C | |
| Front Temperature | 271 - 299 | °C | |
| Processing (Melt) Temp | 277 - 299 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | < 0.345 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Dessicant dryer with -20°F dewpointScrew Speed: Slow to Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALBATCH C 15 70 B2 | RIALTI Srl | PP Copolymer | RIALBATCH |
| Moplen EP640V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| TECAMID™ 66 | Ensinger Inc. | Nylon 66 | TECAMID™ |
| NORYL PPX™ PPX7115F resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL PPX™ |
| LEXAN™ BPL1000 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |