LNP™ THERMOCOMP™ MX06402H compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gi1sU9_LNP-THERMOCOMP-MX06402H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MX06402H is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized, Low Extractable. Also known as: LNP* THERMOCOMP* Compound MF-1004 HS LE Product reorder name: MX06402H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 | g/cm³ | ASTM D792 |
| -- | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 9.0E-3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6400 | MPa | ASTM D638 |
| -- | 5350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 38.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/5 |
| Break 3 | 34.9 | MPa | ASTM D638 |
| Break | 35.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.1 | % | ASTM D638 |
| Yield | 1.8 | % | ISO 527-2/5 |
| Break 5 | 3.5 | % | ASTM D638 |
| Break | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4700 | MPa | ASTM D790 |
| -- 7 | 4700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 65.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 66.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 49 | J/m | ASTM D256 |
| 23°C 9 | 4.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D4812 |
| 23°C 10 | 14 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 12.0 | J | ASTM D3763 |
| -- | 2.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 143 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 134 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 95.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MGF 45 FR 6 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Xuchuan XCW-8030 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Zhongfa PP ZF-ZR1 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Flontech® FT-GL15-NPA-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Tunhe PBT TH6120 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |