Order Products : sales@su-jiao.com
Lutene® XL2802BK
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ghyVuR_Lutene-XL2802BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
Performance:
Description: LUTENE® XL2802BK is a crosslinkable semiconductive shielding compound for conductor and bonded insulation shielding of high voltage power cables. LUTENE® XL2802BK is compatible with both copper and aluminum conductors. LUTENE® XL2802BK was specifically developed to provide a excellent-smoothness surface yielding a more perfect interface between extruded shield and the insulation. As a result, significantly improved cable performance can be expected. LUTENE® XL2802BK has stable volume resistivity charateristics at elevated temperature. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ASTM D1505 |
| Environmental Stress-Cracking Resistance | > 200 | hr | ASTM D1693 |
| Moisture Content | < 500 | ppm | Karl Fisher |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | > 14.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 180 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Retention of Tensile Elongation 3 | > 85 | ppm | ASTM D638 |
| Retention of Tensile Strength 4 | > 90 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -50.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ICEA S-66-524 | ||
| 23°C | < 1.0E+2 | ohms·cm | |
| 90°C | < 3.0E+2 | ohms·cm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Drying Time | 4.0 | hr | |
| Melt Temperature | 100 to 125 | °C |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| 3 . | 135°C, 168 Hr |
| 4 . | 135°C, 168 Hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TATREN® IM 100 85 | Slovnaft Petrochemicals, s.r.o. | PP Impact Copolymer | TATREN® |
| Borealis PP RA130E-2492 | Borealis AG | PP Random Copolymer | Borealis PP |
| Chemical Resources LD10919 | Chemical Resources, Inc. | LDPE | Chemical Resources |
| Karina RED COLOR CONCENTRATE -E 42/250-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KMI PE KM-3416CDMD | KMI Group, Inc. | HDPE | KMI PE |