Plexiglas® Hi-Gloss NTA-3
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ghvP0L_Plexiglas-Hi-Gloss-NTA-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Profile: PLEXIGLAS® Hi-Gloss NTA-3 is a compound with an increased heat deflection temperature based on polymethyl methacrylate (PMMA). Besides the well-known properties of PLEXIGLAS® molding compound, such as
PLEXIGLAS® Hi-Gloss NTA-3 offers the added benefit of
Application: PLEXIGLAS® Hi-Gloss NTA-3 is particularly suitable for injection molding technical components. Owing to its superior brilliance, high-gloss (Class A) surfaces can be obtained in opaque colors. Examples: automotive body parts: window channels, pillar panels |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 2.00 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | > 3.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 106 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 106 | °C | ISO 75-2/A |
| Glass Transition Temperature | 126 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 116 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 675 | °C | IEC 60695-2-13 |
| Fire Rating | B2 | DIN 4102 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 85.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS 1002 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Moplen HP501M | LyondellBasell Industries | PP Homopolymer | Moplen |
| 3M™ Dyneon™ Fluoroplastic FEP 6301Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| ACCUTECH™ HP0339M40CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Karina CLEAR PVC COMPOUND 80/204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |