RTP 6091-85A PA12 BLACK
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ghZOdA_RTP-6091-85A-PA12-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA-12 bondable - manufactured with Santoprene™ TPV technology |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Moisture Content | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 85 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 4.83 | MPa | ASTM D412 |
| Tensile Strength 2(Break) | 8.14 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 400 | % | ASTM D412 |
| Tear Strength 4 | 29.8 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 70°C, 22 hr | 37 | % | ASTM D395B |
| 125°C, 22 hr | 58 | % | ASTM D395B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 263 - 282 | °C | |
| Mold Temperature | 35.0 - 71.1 | °C |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | C mould |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PA 1406 | Premix Oy | Nylon 6 | PRE-ELEC® |
| Tuftec™ H1041 | AKelastomers | SEBS | Tuftec™ |
| Unichem 7884H | Colorite Polymers | PVC, Unspecified | Unichem |
| Hifax CA 1110 G4 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Infino HM-1100F | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |