AKROMID® B3 ICF 30 black (5119)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ghPGK8_AKROMID-B3-ICF-30-black-5119-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties Applications are mechanically high stressed parts in all industries |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.28 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.20 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.1 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 2.0 | 3.5 | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 23000 | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 18000 | 11300 | MPa | ISO 178 |
| Flexural Stress 3 | 290 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 10 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 52 | -- | kJ/m² | |
| 23°C | 55 | 70 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+3 | 1.0E+3 | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ II220 (Compression Molded) | Polymics, Ltd. | PEI | Pyramid™ |
| DINALON® PA 6 15% FV | Grupo Repol | Nylon 6 | DINALON® |
| FRAGOM LCX/3013 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| ESPREE™ NY613GF | SABIC Innovative Plastics | Nylon 6 | ESPREE™ |
| LNP™ LUBRICOMP™ ZFL31XXC compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |