XYLEX™ X8210 resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gh1xPN_XYLEX-X8210-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 265°C/2.16 kg | 10 | g/10 min | |
| 300°C/1.2 kg | 14 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 265°C/2.16 kg | 10.0 | cm³/10min | |
| 300°C/1.2 kg | 13.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.80 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.37 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1480 | MPa | ASTM D638 |
| -- | 1500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.0 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Break 3 | 46.0 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 4.6 | % | ISO 527-2/50 |
| Break 5 | 150 | % | ASTM D638 |
| Break | > 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1600 | MPa | ASTM D790 |
| -- 7 | 1600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 58.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 71 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 200 | J/m | ASTM D256 |
| -20°C | 640 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 10 | 11 | kJ/m² | ISO 180/1A |
| -10°C 11 | 30 | kJ/m² | ISO 180/1A |
| 23°C 12 | 45 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 81.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 79.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 13 | 82.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 81.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ASTM D1525, ISO 306/B120 12 15 |
| -- | 92.0 | °C | ISO 306/B50 |
| CLTE | |||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 8.9E-5 | cm/cm/°C | ISO 11359-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 85.0 | % | ASTM D1003 |
| Haze (2540 µm) | 4.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 76.7 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 249 | °C | |
| Middle Temperature | 238 to 260 | °C | |
| Front Temperature | 243 to 266 | °C | |
| Nozzle Temperature | 243 to 266 | °C | |
| Processing (Melt) Temp | 243 to 266 | °C | |
| Mold Temperature | 43.3 to 60.0 | °C | |
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT7013-720UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| THERMOLAST® K TC8PCN (Series: AD/PA/CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Akulon® K223-P2 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| AKROMID® B3 GF 35 1 natural (2465) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Generic PUR-Ether/MDI | Generic | PUR-Ether/MDI | Generic |