ElectriPlast® EP-CF/PC/ABS
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ggxxAu_ElectriPlast-EP-CF-PC-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JR 8425569 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8460 | MPa | ASTM D638 |
| Tensile Strength (Break) | 99.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 7610 | MPa | ASTM D790 |
| Flexural Strength | 142 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.5E+2 | ohms | ESD STM11.11 |
| Volume Resistivity | 38 | ohms·cm | ASTM D257 |
| Static Decay | 10 | msec | Internal method |
| Surface Resistance | 15 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (No Burn) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 252 | °C | |
| Middle Temperature | 260 | °C | |
| Front Temperature | 263 | °C | |
| Nozzle Temperature | 263 | °C | |
| Mold Temperature | 65.6 | °C | |
| Back Pressure | 2.07 | MPa | |
| Screw Speed | 125 | rpm |
| Injection instructions |
|---|
| Injection Speed: 1 in/sec1st Stage (injection): 2400 psi2nd Stage (molding): 500 psiDecomposition: 0.5 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® 4451XB | Vyncolit N.V. | Phenolic | Vyncolit® |
| Axiall PVC 18760 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| FHR Polypropylene 23N10A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Pearlthane® 11H98 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| Osterlene® HIPS2.63.6 | Osterman & Company | PS (HIPS) | Osterlene® |