TECHNYL® B 218 BLACK 21 N
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ggxSgR_TECHNYL-B-218-BLACK-21-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced copolyamide PA 66/6, heat stabilized, medium viscosity, for injection moulding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 1.4 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.6 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1100 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 95.0 | 50.0 | MPa | |
| Break | 75.0 | 60.0 | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 5.0 | 25 | % | |
| Break | 30 | 400 | % | |
| Flexural Modulus | 3000 | 1200 | MPa | ISO 178 |
| Flexural Stress | 125 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | 5.0 | 16 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 242 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 24 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.030 | 0.10 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 525 | 600 | V | |
| Solution B | 425 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NatureFlex™ 42NP | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| NEOFLON™ M-300P | DAIKIN AMERICA, INC. | PCTFE | NEOFLON™ |
| APEX® 90-A481R-65-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Hostalen PP H1850 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |
| Hostaform® C 9021 AS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |