| Hostacom 65F5-4 conventional melt flow, 2,200 MPa flexural modulus, 40% calcium carbonate-filled polypropylene homopolymer is designed for high stiffness, excellent chemical resistance and improved surface quality of molded parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 48 hr, 3.20 mm) | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 25.0 | MPa | |
| Break | 16.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | |
| Break | 50 | % | |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2299 X 120337 | RTP Company | PEEK | RTP |
| Badamid® PA612 GF33 | Bada AG | Nylon 612 | Badamid® |
| Haysite Plastics HST-II | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Hetron™ F 640 TF | Ashland Performance Materials | Polyester, TS | Hetron™ |
| OMIKRON XLT 50 NAT | TECNOPOL | PP Copolymer | OMIKRON |